Mixed Metal Oxide Ruthenium-Iridium Coated Titanium Plate
- Ru–Ir MMO coating delivers high catalytic activity and long service life.
- Performs reliably across pH 1–14, suitable for both acidic and alkaline environments.
- Low resistance & high current efficiency, enabling low-overpotential electrochemical reactions.
- TA1 titanium plate (1 mm thick) provides excellent strength and corrosion resistance.
- Available in 25×25 mm, 50×50 mm, and 100×100 mm sizes, with full customization options.
Our Mixed Metal Oxide (MMO) Ruthenium–Iridium Coated Titanium Electrodes are engineered for demanding industrial and research applications requiring superior durability, conductivity, and chemical stability. The Ru–Ir catalytic coating ensures low electrical resistance, high current efficiency, and reduced overpotentials—critical for processes such as water splitting, electrochemical synthesis, OER, and HER applications.
Built on high-quality TA1 titanium, these electrodes maintain excellent stability across a wide voltage range and function effectively in both acidic and alkaline environments (pH1–14). The MMO coating is applied through a controlled thermal decomposition process after precision sandblasting, ensuring strong adhesion and long operational life
Specifications
| Parameter | Value |
|---|---|
| Titanium Grade | TA1 |
| Plate Thickness | 1 mm |
| Deposition Method | Thermal decomposition |
| Pre-treatment | Sandblasting |
| Coating Ratio (Ru/Ir) | 8 : 2 |
| Coating Thickness | 10 µm |
| Noble Metal Loading | 10 g/m² |
| Max. Current Density | 2000 A/m² |
| Typical Operating Current Density | 300 A/m² |
| Available Sizes | 25×25 mm, 50×50 mm, 100×100 mm, custom |
| pH Range | 1 – 14 |
| Max. Fluoride Ion Content | <1 ppm |
| Quantity per Pack | 10 pieces |